Uaea PC Ribs loloʻu

Faamatalaga puupuu:

O mea: 82B, 77B

Le lapoa uaea (mm): 4.0 ~ 12,0

Le Malosi Tensile (faasao): 1290 ~ 1860

O le pusa: teu i coil (1Ton -3 tone)

O le Talosaga: uaea uamea pc malologa Low faaaoga mo fausaga uamea prestressed, prestressed

ma posttensioning tekinolosi i tetele, auala ma laiti ituaiga o foliga eseese o PC

fausaga, e pei o le fausiaina inisinia tau le va o auala o nofoaafi tele fua, alatele

Good quantity and  performance


Faamatalaga oloa

pine o oloa

Dia: 4mm-9mm
Standard: GB / T5223-2002, BS5896, ASTM A421
Min.breaking avega: 1470-1860MPA
e faaaoga faapitoa uaea PC pei PCCP paipa, totoga, fuafuati faamalosia ausilali mo eg fausaga sima

umi folasia alalaupapa i nofoaafi, alatele, sleeper ma uaea e lagonaina o alalaupapa aga tele

Loloʻu RIBS PC uaea

Lapoa / mm

Faapalepale / mm

Eria / mm 2

mamafa-g faʻalemafaufau / m

Uaea tele Cross-sectional

RibPieces

LayLength (Lg) / mm

Faavae-roundDia (D1) / mm

OutioneDia (D) / mm

RibWidth (jk) / mm

RibHeight (jg) / mm

4,00

0,04

12,57

98,6

3,85 ± 0,055

 4,25 ± 0,055

0,90 ~ 1,30

0,15 ~ 0,25

4

24-30

4,80

0.05

18,10

142

 4,60 ± 0. 055

 5,10 ± 0,055

1,30 ~ 1,70

0,20 ~ 0,30

28-36

5.00

19,63

154

4,08 ± 0. 055

 5,30 ± 0,055

1,30 ~ 1,70

0,20 ~ 0,30

28-36

5,25

21,65

170

5,05 ± 0. 055

 5,55 ± 0,055

1,40 ~ 1,80

0,20 ~ 0,30

28-38

6,00

28,27

222

5,80 ± 0. 055

 6,30 ± 0,055

1,60 ~ 2.00

0,30 ~ 0,40

30-38

6,25

30,68

241

6,00± 0,055

 6,70 ± 0,055

1,60 ~ 2.00

0,30 ~ 0,40

30-40

7,00

38,48

302

6,73 ± 0,055

 7,46 ± 0,100

1,80 ~ 2,20

0,30 ~ 0,40

35-45

7,50

44,18

347

 7,25 ± 0,055

7,95 ± 0,055

1,90 ~ 2,30

0,30 ~ 0,40

40-50

8,00

0,06

50,26

394

 7,75 ± 0,055

 8,45 ± 0,100

2.00 ~ 2,40

0,30 ~ 0,40

40-50

9,00

63,62

499

8,75 ± 0,055

 9,45 ± 0,055

2.10 ~ 2.70

0,30 ~ 0,40

42-52

9,50

70,88

556

 9,25 ± 0,100

 9,25 ± 0,055

2,20 ~ 2,80

0,30 ~ 0,40

44-55

10.00

78,54

616

 9,75 ± 0,055

 9,75 ± 0,055

2.50 ~ 3,00

0,30 ~ 0,40

45-58

12.00

113,1

888

11,60 ± 0,055

 12,20 ± 0,100

2,80 ~ 3,20

0,30 ~ 0,40

50-65

 

Lapoa / mm

laiti

Tensile

Malosi / faasao

fua

Malosi / faasao

Elongation

Lo = 200mm /%

180oBending

Times

taimi pāganoa

Times

punou

Faataamilosaga / mm

tuutuuga

%

4,00

1470

1570

1670

1770

1860

1290

1380

1470

1560

1640

3.5

3

10

avega uluai

le 70% o

laiti

solia

mālosi

2.5

4,80

4

15

5.00

5,25

6,00

6,25

20

7,00

7,50

1470 1570

1670 1770

1290 1380

1470 1560

8,00

9,00

1470 1570

1670

1290 1380

1470

25

9,50

10.00

1470 1570

1290 1380

12.00

30